Spring Steel Wire | Stahl-Becker

Month	Spring steel Strip 1.4310	Spring steel strip 1.4310 (increased Mo)	Spring steel wire 1.4310	Stainless steel strip 1.4301	Precision steel strip 1.4301	Stainless steel wire 1.4301	Precision steel strip 1.4404	Stainless steel wire 1.4404
2024
Dec	2,34	2,66	2,49	2,06	2,48	2,64	4,14	4,36
Nov	2,37	2,68	2,52	2,10	2,51	2,68	4,16	4,38
Oct	2,25	2,56	2,44	1,99	2,39	2,59	3,99	4,25
Sept	2,28	2,60	2,50	2,02	2,42	2,66	4,04	4,33
Aug	2,40	2,74	2,62	2,12	2,55	2,79	4,30	4,58
July	2,58	2,92	2,78	2,29	2,75	2,97	4,58	4,83
june	2,60	2,91	2,80	2,31	2,78	3,00	4,51	4,77
May	2,44	2,73	2,61	2,16	2,59	2,78	4,20	4,42
Apr	2,39	2,69	2,56	2,12	2,54	2,73	4,16	4,38
March	2,29	2,58	2,44	2,02	2,42	2,59	3,96	4,17
Feb	2,21	2,51	2,42	1,95	2,34	2,57	3,89	4,17
Jan	2,25	2,50	2,51	1,99	2,38	2,67	3,79	4,13
2023
Dec	2,32	2,62	2,66	2,06	2,47	2,84	4,05	4,46
Nov	2,42	2,76	2,79	2,14	2,57	2,99	4,33	4,82
Oct	2,48	2,83	2,90	2,20	2,64	3,11	4,51	5,07
Sept	2,46	2,81	2,85	2,19	2,63	3,07	4,47	4,99
Aug	2,49	2,81	2,88	2,21	2,65	3,10	4,39	4,91
July	2,68	3,00	3.08	2,38	2,86	3.32	4,66	5.18
june	2,82	3,13	3,26	2,51	3,01	3,51	4,86	5,40
May	2,84	3,21	3,33	2,53	3,03	3,58	5,05	5,60
Apr	2,96	3,58	3,43	2,65	3,17	3,70	6,05	6,63
March	3,24	3,87	3,75	2,90	3,48	4,05	6,57	7,25
Feb	3,33	3,77	3,84	2,99	3,59	4,16	6,10	6,74
Jan	3,25	3,58	3,79	2,92	3,50	4,11	5,61	6,27
2022
Dec	3,01	3,30	3,58	2,69	3,22	3,87	5,08	5,80
Nov	3,03	3,30	3,56	2,68	3,21	3,83	5,02	5,70
Oct	3,01	3,24	3,58	2,65	3,17	3,83	4,80	5,50
Sept	2,95	3,14	3,51	2,58	3,10	3,77	4,61	5,28
Aug	3,07	3,30	3,58	2,73	3,28	3,84	4,92	5,49
July	3,53	3,74	4,18	3,14	3,77	4,49	5,53	6,28
june	3,62	3,86	4,56	3,22	3,85	4,91	5,67	6,85
May	4,30	4,52	4,78	3,84	4,61	5,14	6,67	7,14
Apr	3,64	3,86	4,15	3,25	3,90	4,45	5,73	6,27
March	2,99	3,22	3,42	2,66	3,19	3,65	4,79	5,25
Feb	2,80	3,02	3,20	2,48	2,97	3,40	4,51	4,96
Jan	2,74	2,97	3,12	2,42	2,91	3,30	4,40	4,81
2021
Dec	2,62	2,85	3,05	2,31	2,77	3,22	4,26	4,72
Nov	2,47	2,70	2,85	2,19	2,62	3,02	4,06	4,47
Oct	2,47	2,71	2,71	2,19	2,63	2,88	4,11	4,37
Sept	2,44	2,60	2,64	2,17	2,60	2,81	4,02	4,24
Aug	2,28	2,52	2,54	2,02	2,43	2,70	3,83	4,10
July	2,14	2,33	2,35	1,90	2,28	2,49	3,48	3,73
june	2,09	2,21	2,26	1,85	2,23	2,41	3,19	3,38
May	2,02	2,12	2,10	1,79	2,15	2,23	3,05	3,14
Apr	2,08	2,20	2,06	1,85	2,22	2,19	3,18	3,17
March	2,08	2,17	2,09	1,85	2,22	2,23	3,15	3,17
Feb	1,93	2,01	2,01	1,72	2,06	2,15	2,91	3,00
Jan	1,78	1,86	1,85	1,59	1,91	1,98	2,72	2,80
2020
Dec	1,69	1,78	1,76	1,52	1,82	1,88	2,61	2,68
Nov	1,62	1,70	1,68	1,45	1,74	1,80	2,48	2,55
Oct	1,63	1,70	1,69	1,46	1,75	1,81	2,48	2,54
Sept	1,53	1,59	1,59	1,37	1,64	1,70	2,30	2,37
Aug	1,53	1,59	1,56	1,37	1,64	1,67	2,29	2,33
July	1,52	1,60	1,55	1,36	1,63	1,65	2,31	2,35
june	1,53	1,62	1,52	1,36	1,64	1,61	2,36	2,34
May	1,44	1,53	1,41	1,28	1,53	1,49	2,22	2,19
Apr	1,46	1,56	1,46	1,30	1,56	1,55	2,32	2,34
March	1,53	1,66	1,57	1,37	1,64	1,66	2,49	2,53
Feb	1,62	1,72	1,67	1,45	1,74	1,78	2,54	2,59
Jan	1,61	1,70	1,65	1,44	1,72	1,76	2,51	2,55
2019
Dec	1,79	1,87	1,82	1,61	1,93	1,95	2,78	2,81
Nov	1,92	2,04	1,95	1,73	2,08	2,10	3,10	3,14
Oct	1,92	2,05	1,98	1,73	2,07	2,13	3,11	3,19
Sept	1,74	1,87	1,78	1,56	1,87	1,90	2,83	2,88
Aug	1,55	1,69	1,57	1,38	1,66	1,67	2,55	2,57
July	1,54	1,68	1,55	1,36	1,63	1,64	2,51	2,53
june	1,56	1,70	1,59	1,38	1,66	1,68	2,55	2,58
May	1,63	1,78	1,67	1,45	1,74	1,77	2,66	2,71
Apr	1,61	1,75	1,63	1,43	1,72	1,73	2,64	2,66
March	1,52	1,65	1,55	1,35	1,62	1,64	2,46	2,48
Feb	1,39	1,53	1,42	1,23	1,47	1,50	2,28	2,31
Jan	1,45	1,59	1,48	1,28	1,53	1,56	2,37	2,41
2018
Dec	1,55	1,69	1,57	1,37	1,64	1,66	2,51	2,53
Nov	1,60	1,73	1,66	1,41	1,69	1,76	2,57	2,64
Oct	1,63	1,77	1,70	1,44	1,73	1,79	2,62	2,69
Sept	1,72	1,86	1,79	1,52	1,83	1,90	2,74	2,83
Aug	1,79	1,90	1,85	1,58	1,90	1,96	2,77	2,84
July	1,86	1,98	1,93	1,65	1,98	2,05	2,90	2,98
june	1,73	1,86	1,79	1,53	1,83	1,89	2,73	2,80
May	1,62	1,75	1,65	1,43	1,72	1,74	2,58	2,61
Apr	1,59	1,73	1,58	1,41	1,69	1,67	2,57	2,57
March	1,53	1,66	1,54	1,35	1,62	1,63	2,5	2,49
Feb	1,49	1,61	1,54	1,32	1,58	1,62	2,39	2,35
Jan	1,47	1,55	1,52	1,29	1,55	1,59	2,24	2,21
2017
Dec	1,54	1,62	1,59	1,36	1,64	1,67	2,32	2,3
Nov	1,44	1,52	1,41	1,26	1,51	1,48	2,14	2,08
Oct	1,42	1,50	1,37	1,25	1,50	1,45	2,14	2,07
Sept	1,26	1,34	1,26	1,11	1,33	1,32	1,92	1,88
Aug	1,26	1,33	1,25	1,11	1,33	1,32	1,87	1,82
July	1,36	1,44	1,38	1,19	1,43	1,45	2,00	1,97
june	1,42	1,52	1,46	1,24	1,49	1,53	2,14	2,14
May	1,54	1,64	1,59	1,35	1,62	1,67	2,32	2,35
Apr	1,66	1,74	1,70	1,46	1,75	1,79	2,43	2,45
March	1,60	1,67	1,64	1,40	1,69	1,72	2,31	2,32
Feb	1,64	1,70	1,57	1,43	1,72	1,65	2,34	2,23
Jan	1,51	1,58	1,45	1,34	1,61	1,54	2,25	2,15
2016
Dec	1,35	1,41	1,31	1,20	1,44	1,39	2,02	1,95
Nov	1,24	1,31	1,19	1,10	1,32	1,27	1,89	1,80
Oct	1,16	1,22	1,10	1,03	1,23	1,17	1,77	1,71
Sept	1,23	1,29	1,14	1,09	1,31	1,22	1,86	1,78
Aug	1,14	1,20	1,03	1,01	1,22	1,10	1,74	1,62
July	1,02	1,10	0,88	0,90	1,08	0,93	1,60	1,45
june	1,03	1,09	0,95	0,91	1,10	1,01	1,55	1,45
May	0,97	1,00	0,89	0,85	1,02	0,94	1,41	1,31
Apr	0,98	1,01	0,93	0,87	1,04	0,99	1,43	1,37
March	0,94	0,97	0,88	0,83	0,99	0,93	1,36	1,30
Feb	0,99	1,02	0,93	0,87	1,05	0,99	1,43	1,39
Jan	1,05	1,07	1,00	0,93	1,11	1,07	1,48	1,44
2015
Dec	1,13	1,15	1,11	1,00	1,20	1,18	1,60	1,58
Nov	1,12	1,15	1,11	1,00	1,20	1,18	1,62	1,61
Oct	1,11	1,14	1,12	0,99	1,18	1,19	1,61	1,63
Sept	1,22	1,25	1,27	1,08	1,30	1,35	1,78	1,85
Aug	1,31	1,35	1,37	1,17	1,40	1,45	1,93	2,01
July	1,39	1,56	1,47	1,24	1,49	1,57	2,11	2,24
june	1,43	1,49	1,55	1,28	1,53	1,65	2,19	2,36
May	1,42	1,50	1,54	1,27	1,53	1,64	2,22	2,39
Apr	1,47	1,54	1,62	1,32	1,58	1,73	2,28	2,49
March	1,47	1,55	1,61	1,32	1,59	1,73	2,31	2,51
Feb	1,44	1,52	1,56	1,29	1,55	1,67	2,27	2,45
Jan	1,47	1,55	1,64	1,33	1,59	1,75	2,31	2,56
2014
Dec	1,39	1,48	1,54	1,25	1,50	1,65	2,22	2,44
Nov	1,47	1,56	1,63	1,32	1,58	1,75	2,35	2,59
Oct	1,60	1,72	1,78	1,44	1,73	1,91	2,63	2,91
Sept	1,55	1,67	1,73	1,40	1,68	1,58	2,56	2,84
Aug	1,55	1,67	1,74	1,40	1,67	1,86	2,59	2,84
July	1,55	1,69	1,73	1,39	1,67	1,85	2,62	2,90
june	1,51	1,62	1,71	1,36	1,63	1,83	2,50	2,80
May	1,32	1,41	1,50	1,19	1,42	1,60	2,13	2,39
Apr	1,20	1,27	1,38	1,07	1,29	1,47	1,90	2,14
March	1,18	1,25	1,33	1,05	1,26	1,41	1,86	2,07
Feb	1,16	1,24	1,30	1,03	1,24	1,38	1,83	2,03
Jan	1,12	1,20	1,26	1,00	1,20	1,34	1,77	1,98
2013
Dec	1,16	1,24	1,30	1,03	1,24	1,38	1,83	2,04
Nov	1,12	1,20	1,27	1,00	1,20	1,35	1,76	1,98
Oct	1,17	1,25	1,32	1,05	1,26	1,40	1,84	2,05
Sept	1,20	1,27	1,34	1,07	1,28	1,42	1,87	2,07
Aug	1,19	1,27	1,36	1,06	1,27	1,44	1,89	2,14
July	1,27	1,36	1,47	1,14	1,36	1,56	2,04	2,32
june	1,34	1,44	1,54	1,20	1,44	1,63	2,16	2,44
May	1,43	1,52	1,62,1	28	1,54	1,72	2,27	2,54
Apr	1,42	1,52	1,62	1,28	1,53	1,73	2,29	2,57
March	1,47	1,56	1,67	1,32	1,58	1,78	2,36	2,65
Feb	1,45	1,55	1,65	1,30	1,56	1,76	2,36	2,64
Jan	1,64	1,56	1,66	1,31	1,57	1,78	2,36	2,64
2012
Dec	1,39	1,48	1,58	1,25	1,50	1,69
Nov	1,51	1,61	1,76	1,36	1,63	1,88
Oct	1,50	1,62	1,72	1,34	1,61	1,83
Sept	1,48	1,58	1,70	1,32	1,58	1,81
Aug	1,54	1,66	1,78	1,38	1,65	1,90
July	1,58	1,71	1,82	1,41	1,70	1,94
june	1,58	1,71	1,82	1,42	1,70	1,93
May	1,58	1,71	1,78	1,42	1,70	1,90
Apr	1,63	1,77	1,87	1,47	1,76	2,00
March	1,73	1,86	2,00	1,57	1,88	2,14
Feb	1,65	1,78	1,91	1,49	1,79	2,04
Jan	1,50	1,62	1,72	1,34	1,61	1,84
2011
Dec	1,50	1,63	1,73	1,35	1,62	1,85
Nov	1,56	1,69	1,79	1,40	1,68	1,91
Oct	1,68	1,81	1,94	1,51	1,81	2,07
Sept	1,75	1,88	2,04	1,58	1,90	2,18
Aug	1,80	1,93	2,11	1,62	1,95	2,26
July	1,78	1,92	2,07	1,60	1,92	2,21
june	1,93	2,07	2,23	1,74	2,09	2,39
May	2,03	2,19	2,36	1,84	2,21	2,53
Apr	2,14	2,30	2,49	1,94	2,33	2,67
March	2,23	2,40	2,55	2,02	2,41	2,74
Feb	2,12	2,29	2,43	1,92	2,30	2,61
Jan	1,96	2,12	2,28	1,77	2,12	2,44
2010
Dec	1,83	1,99	2,13	1,66	1,99	2,28
Nov	1,89	2,05	2,17	1,71	2,05	2,33
Oct	1,91	20,8	2,22	1,72	2,07	2,38
Sept	1,81	1,96	2,12	1,63	1,96	2,27
Aug	1,74	1,91	20,4	1,57	1,88	2,18
July	1,85	2,02	2,18	1,67	2,00	2,37
june	2,05	2,24	2,41	1,86	2,23	2,58
May	1,98	2,16	2,31	1,80	2,15	2,48
Apr	1,60	1,78	1,86	1,44	1,74	2,00
March	1,32	1,48	1,54	1,20	1,44	1,65
Feb	1,25	1,38	1,46	1,13	1,36	1,57
Jan	1,06	1,14	1,24	0,95	1,15	1,33
2009
Dec	1,13	1,21	1,31	1,02	1,23	1,41
Nov	1,17	1,28	1,32	1,06	1,27	1,43
Oct	1,18	1,31	1,38	1,07	1,29	1,48
Sept	1,20	1,36	1,40	1,09	1,31	1,51
Aug	0,99	1,08	1,11	0,89	1,07	1,20
July	0,86	0,95	0,99	0,78	0,94	1,07
june	0,74	0,82	0,89	0,67	0,80	0,95
May	0,67	0,74	0,85	0,60	0,72	0,91
Apr	0,72	0,80	0,93	0,64	0,76	0,99
March	0,83	0,92	1,15	0,74	0,89	1,22
Feb
Jan
All values are €/Kg

Stainless Spring Steel Wire (1.4310)
Patented Drawn Spring Steel Wire (SH/DH)

You can order the stainless spring steel wire as coils, spools or straightened bars. The standard lengths of the straightened rods are one, two or three meters.
The straightened bars can be cut in length according to your wishes.
Beside steel grade 1.4310 we are able to deliver 1.4401 (AISI 316) and 1.4404 (AISI 316L)!

Material	Material Number	DIN Material Code	US Material Code (AISI/SAE)
X10CrNi18-8	1.4310	X 12 CrNi 17-7	~ 302

Material Standard	(BS EN 10270-3) BS EN ISO 6931-1
Dimension standard	BS EN ISO 6931-1 (BS EN 10270-3) DIN EN 10218-2 DIN EN 10278
Products	Wire (coils) Straightened rods Wire (spools)
Dimensions	coils/spools: 0,30 mm to 15,00 mm diameter bars: 0,30 mm to 15,00 mm diameter
Tensile strength (Rm)	1250 to 2200 N/mm², depending on the diameter of the wire
Surface	matt shining finish or polished, partial ground and polished
Information	The maximum possible temperature of usage is up to 250°C (dependent upon load). Change in standard: The EN 10270-3 standard was replaced by ISO 6931-1 in November 2020. The following changes have resulted: the material number has changed (the material short name has been retained) lower limit values for tensile strength have been added additional tolerance classes for the diameter of wire in coils and on spools have been introduced.
Heat Treatment	after the forming process of the spring the tensile strength can be increased by heat treatment (a plus of approx. 150 N/mm²) the heat treatment also smoothes out the tensions of the forming process the EN-Standard recommendation reaches from annealing at 250°C for 4 hours to 425°C for 30 minutes; cooling down by air

Chemical analysis (in %) according to DIN EN ISO 6931-1, table 1

Material Code	1.4310 \| 4310-301-00-I
C	0,05 - 0,15
Si	≤ 2,00
Mn	≤ 2,00
P	≤ 0,045
S	≤ 0,015
Cr	16,00 - 19,00
Mo	≤ 0,80
Ni	6,00 - 9,50
N	≤ 0,10

Additional Informtion

MECHANICAL PROPERTIES

E-Modulus in GPa (Gigapascal) at room temperature (guide value) according EN 10270-3 table A.1 (excerpt for material 1.4310)

Shear Modulus in GPa (Gigapascal) at room temperature (guide value) according EN 10270-3 table A.1 (excerpt for material 1.4310)

Tensile strength according EN 10270-3, table 2 (excerpt for material 1.4310)

E-Modulus in GPa (Gigapascal) at room temperature (guide value) according ISO 6931-1 table A.1 (excerpt for material X10CrNi18-8)

Shear Modulus in GPa (Gigapascal) at room temperature (guide value) according ISO 6931-1 table A.1 (excerpt for material X10CrNi18-8)

Tensile strength according ISO 6931-1, table 2 (excerpt for material X10CrNi18-8)

TOLERANCES

Diameter tolerance according EN 10270-3, table 5

Tolerance of length according EN 10270-3, table 6

Diameter tolerance of straight rods according ISO 6931-1, table 5

Diameter tolerance of wire on coils and spools according ISO 6931-1, table 5

Tolerance of length according ISO 6931-1, table 6

Show Data Sheet

erstelle PDF...

You can order the patented drawn spring steel wire as coils, spools or straightened bars. The standard lengths of the straightened rods are one, two or three meters.
The straightened bars can be cut in length according to your wishes.

Material	Material Number	DIN Material Code	Other Descriptions
SH	-	Sorte C	Piano wire
DH	-	Sorte D	Piano wire

Material Standard	DIN EN 10270-1
Dimension standard	DIN EN 10270-1 DIN EN 10218-2
Products	Wire (coils) Wire (spools) Straightened rods
Dimensions	Coils/spools: 0,20 mm to 8,00 mm diameter Bars: approx. 0,50 mm to 16,00 mm diameter
Tensile strength (Rm)	1300 - 2940 N/mm² depending on the diameter of the wire
Surface	matt gray, polished on request
Coating	phosphated
Information	Most common quality for springs Suitable for tension springs, pressure springs and torsion springs with a high static load and a low dynamic load The E-Modulus is approx. 206 Gigapascal, the shear modulus is approx. 81,5 Gigapascal

Chemical analysis (in %) according to DIN EN 10270-1, table 2

Material Code	SH	DH
C	0,35 - 1,00	0,45 - 1,00
Si	0,10 - 0,30	0,10 - 0,30
Mn	0,40 - 1,20	0,40 - 1,20
P	≤ 0,035	≤ 0,020
S	≤ 0,035	≤ 0,025
Cu	≤ 0,20	≤ 0,12
Remark	The analysis also applies to material SM and SL.	The analysis also applies to material DM.

Additional Informtion

TOLERANCES

Tolerances of diameter according EN 10270-1, table 3 (excerpt)

Tolerance of the diameter of straightened rods according EN 10270-1, table 8

Tolerance in length according EN 10270-1, table 7

MECHANICAL PROPERTIES

Tensile strengths according EN 10270-1, table 3

Show Data Sheet

erstelle PDF...

Alloy Surcharges

Chemical analysis (in %) according to DIN EN ISO 6931-1, table 1

Additional Informtion

Chemical analysis (in %) according to DIN EN 10270-1, table 2